in the present research work, the flexural modulus and strength of glass fiber-epoxy resin and carbon fiber-epoxy resin composites have been enhanced through fiber tension during curing of the polymeric resin. this study showed that the tension applied on the fibers increased the flexural modulus of the glass-epoxy composites up to 12% and the flexural strength up to 19%. the flexural modulus a...

In the present research work, the flexural modulus and strength of glass fiber-epoxy resin and carbon fiber-epoxy resin composites have been enhanced through fiber tension during curing of the polymeric resin. This study showed that the tension applied on the fibers increased the flexural modulus of the glass-epoxy composites up to 12% and the flexural strength up to 19%. The flexural modulus a...

The focus of this work is the evaluation of the physical compatibility between an epoxy resin used as a matrix and an oxidized, unsized carbon fiber, and between this same epoxy resin and glassy carbon. For this purpose, carbon fibers, glassy carbon and epoxy resin have been assigned Hansen solubility (cohesion) parameters (HSP) by analysis of their interactions with a set of well-defined liqui...

A maximum of 91% recovery of interfacial shear strength (IFSS) is achieved for carbon fiber/epoxy interfaces functionalized with capsules containing reactive epoxy resin and ethyl phenyl acetate (EPA). We find a binder is necessary to improve the retention of capsules on the carbon fiber surface. Two different methods for applying the binder to the carbon fiber surface are investigated. Healing...

In this study, carbon nano fibers (CNFs) were mixed into epoxy resin through a magnetic stirrer and again mixed using ultra sonicator. Using hand layup technique, biaxial braided fiber composites were prepared with unfilled, 0.2, 0.5 and 1 wt% CNF. Tensile test and shear test was performed to identify the tensile strength and shear strength of the composites. Fractured surface of the tensile sp...

External bonding of carbon fiber sheets has become a popular technique for strengthening concrete structures all over the world. Epoxy adhesive, which is used to bond the carbon fiber sheets and concrete, deteriorates rapidly when being exposed to high temperatures. This paper presents a high-temperature-resistant modified magnesia-phosphate cement (MPC) with the compressive strength that does ...

Non covalent functionalization by π stacking was accomplished by treating multi walled carbon nanotubes (MWNTs) through the use of Kentera, a conjugate rigid rod polymer. The functionalized MWNTs were then introduced into the epoxy resins through a combination of shear and elongation forces. The resulting epoxy resin (containing MWNTs) was then impregnated with carbon fiber under hot-melt condi...

................................................................................................................................................... vi 1. Background ........................................................................................................................................... 1 1.1 Carbon Fiber ............................................................................

Electrospun veils from copolyethersulfones (coPES) were prepared as soluble interlaminar veils for carbon fiber/epoxy composites. Neat, resin samples were impregnated into coPES veils with unmodified resin, while dry carbon fabrics were covered with electrospun veils and then infused with the unmodified epoxy resin to prepare reinforced laminates. The thermoplastic content varied from 10 wt% to...

Matrix resins of carbon fiber-epoxy composites with different numbers of epoxy functional groups were prepared, and their properties were compared to optimize the matrix resin composition. To understand the bonding strengths between the carbon fiber and epoxy resins in monofilaments and micro-sized resin beads, the interfacial shear strength (IFSS) was measured using the microdroplet technique....